Synthesis and characterization of silica coated magnetic iron oxide nanoparticles

7 34 0
Synthesis and characterization of silica coated magnetic iron oxide nanoparticles

Đang tải... (xem toàn văn)

Thông tin tài liệu

Advances in nanotechnology in recent years have led to a number of diverse applications of nanomaterials. Magnetic iron oxide nanoparticles (Fe3O4 NPs), a representative of magnetic nanomaterials, have gained much attention of many researchers all over the world due to their unique properties such as superparamagnetism, biocompatibility and high magnetic saturation.

Vietnam Journal of Science and Technology 57 (3A) (2019) 160-166 doi:10.15625/2525-2518/57/3A/14203 SYNTHESIS AND CHARACTERIZATION OF SILICA COATED MAGNETIC IRON OXIDE NANOPARTICLES Minh-Tri Nguyen-Le1, Dinh Tien Dung Nguyen1, Sophia Rich1, 3, Ngoc Tram Nguyen1, 3, Cuu Khoa Nguyen1, Dai Hai Nguyen1, 2, * Institute of Applied Materials Science, Vietnam Academy of Science and Technology, Thanh Loc 29, District 12, Ho Chi Minh City Graduate University of Science and Technology, Vietnam Academy of Science and Technology, 18 Hoang Quoc Viet, Cau Giay, Ha Noi Tra Vinh University, No 126, Nguyen Thien Thanh, Ward 5, Tra Vinh city, Tra Vinh province * Email: nguyendaihai0511@gmail.com Received: 13 August 2019; Accepted for publication: 30 September 2019 Abstract Advances in nanotechnology in recent years have led to a number of diverse applications of nanomaterials Magnetic iron oxide nanoparticles (Fe3O4 NPs), a representative of magnetic nanomaterials, have gained much attention of many researchers all over the world due to their unique properties such as superparamagnetism, biocompatibility and high magnetic saturation With such properties, Fe3O4 NPs can be exploited in many fields, particularly biomedicine related fields such as cellular therapy, tissue repair, drug delivery, magnetic resonance imaging, hyperthermia and magnetofection However, owing to their self-aggregation of Fe3O4 NPs, it is necessary to coat Fe3O4 NPs with a stable and biocompatible silica layer Therefore, in this report, Fe3O4 NPs were synthesized via a co-precipitation method using iron (II)/ iron (III) chloride, ammonia and trisodium citrate Then, the silica layer was coated onto Fe3O4 NPs through the hydrolysis and condensation of tetraethyl orthosilicate (TEOS) in ethanol The as-synthesized samples were characterized with the infrared (IR) spectroscopy, Xray diffraction (XRD), thermogravimetric analysis (TGA), vibrating sample magnetometer (VSM), transmission electron microscopy (TEM) and dynamic light scattering (DLS) The results proved that silica was successfully coated on Fe3O4 NPs The particle sizes measured by TEM were found to be about 12 nm in diameter for Fe3O4 NPs and 45 nm in diameter for silica coated Fe3O4 (SiO2@Fe3O4) NPs, while the dynamic diameters measured by DLS for Fe3O4 NPs and SiO2@Fe3O4 NPs were 15.7 and 65.8 nm, respectively Both Fe3O4 NPs and SiO2@Fe3O4 NPs were superparamagnetic materials in which Fe3O4 NPs have higher magnetic saturation (45.8 emu/g) than the other (13.4 emu/g) Keywords: Fe3O4 nanoparticles; silica; superparamagnetic Classification numbers: 2.2.1, 2.4.3, 2.10.2 INTRODUCTION Synthesis and characterization of silica coated magnetic iron oxide nanoparticles Recently, advances in nanotechnology have led to a number of diverse applications of nanomaterials Magnetic iron oxide nanoparticles (Fe3O4 NPs), a representative of magnetic nanomaterials, have gained much attention of many researchers all over the world due to their exceptional properties over the bulk materials such as superparamagnetism, biocompatibility and high magnetic saturation It is noteworthy that bulk magnetic materials are composed of microscopic crystalline grains (also known as polycrystalline) Unlike bulk magnetic materials, magnetic nanomaterials, with the size between nm and 100 nm, are single-domain materials which are uniformly magnetized to their saturation magnetization Several nanoparticles can be synthesized from oxides and alloys of Fe, Ni, Co, etc In the last decades, much research has been developed to the synthesis of Fe3O4 NPs due to their biocompatibility, superparamagnetic behavior and chemical stability Mahdavi et al reported synthesis of superparamagnetic Fe3O4 NPs with the average particle size of about 16.5 nm and saturation magnetization of 80 emu.g−1[1] For drug delivery, poly(ethyleneglycol)-modified superparamagnetic Fe3O4 NPs with the average size of 40–50 nm and saturation magnetization of 45-50 emu.g−1 were also reported by Gupta et al [2] In addition to drug delivery, other applications of Fe3O4 NPs such as cell labelling, hyperthermia and MRI contrast enhancement were also demonstrated [3-5] However, owing to large surface-to-volume ratio, Fe3O4 NPs possesses high surface energy which results in aggregation of Fe3O4 NPs so as to minimize the surface energy In order to prevent them from loss of magnetism and dispersibility due to the aggregation and oxidation in air, it is necessary to coat them with some protective layers such as organic molecules, including small organic molecules or surfactants, polymers, and biomolecules, or coating with an inorganic layer, such as silica, metal or nonmetal elementary substance, metal oxide or metal sulfide [6] Among them, surface coating of Fe3O4 NPs with silica not only stabilize the Fe3O4 NPs but also enhance surface functionalization through silanol groups, which is important for biomedical applications [7] Therefore, herein, we report one-pot synthesis of SiO2@Fe3O4 NPs through both coprecipitation of Fe (II) and Fe (III) ions, and hydrolysis and condensation of TEOS MATERIALS AND METHODS 2.1 Materials and characterization For synthesis of the NPs, FeCl2.4H2O (98 %) and FeCl3.6H2O (98 %) were purchased from Merck Tetraethyl orthosilicate (TEOS, 98 %) was purchased from Sigma-Aldrich Ethanol (99 %) was purchased from Scharlau Ammonium hydroxide ( 30-33% NH3 in H2O) and trisodium citrate (TSC, 99 %) were obtained from a China company Deionized (DI) water with resistance of 18 MΩ cm was used in all the experiments All chemicals were used without further purification For characterization, the structure morphology of synthesized Fe3O4 NPs was studied through a transmission electron microscope (TEM, JEOL JEM-1400, 100 kV) The particle size distribution of the NPs was recorded on a Zetasizer Nano ZS (ZEN 36000, Malvern Instruments, UK) via dynamic light scattering (DLS) In order to study the crystalline structure, X-ray diffraction (XRD) was conducted on a Rigaku X-ray diffractometer with Cu Kα radiation (λ = 0.154056 nm) Moreover, the functional groups of the Fe3O4 NPs, SiO2@Fe3O4 NPs and their intermediates generated during the synthesis were studied through FT-IR/NIR 161 Minh-Tri Nguyen-Le et al Spectroscopy (Frontier) Thermogravimetric analysis (TGA) was also performed on TGA-DSC Mettler Toledo 3+ The magnetic properties of magnetic as-synthesized materials were investigated using Vibrating Sample Magnetometer (DMS 880) 2.2 Synthesis of Fe3O4 NPs Briefly, 0.796 g FeCl2.4H2O and 2.164 g FeCl3.6H2O were dissolved into 40 mL of DI water under vigorous stirring and N2 purging for 30 minutes Then, 13 mL of 10 % NH3 was added into the mixture The color of the obtained solution changed from orange to brown, followed by black, indicating the formation of Fe3O4 NPs The obtained Fe3O4 NPs were separated from the solution by using a magnet, and then washed with DI water for several times Finally, the products were passed through freeze-drying in hr 2.3 Surface modification of Fe3O4 NPs with TSC The surface functionalization of Fe3O4 NPs was carried out by mixing the obtained Fe3O4 NPs into 200 mL of 0.5 M TSC solution at 80 oC in hr The obtained solids (denoted as TSC@Fe3O4 NPs) were separated from the solution by using a magnet, washed with DI water for several times, and then dispersed into DI water for further use 2.4 Surface coating of Fe3O4 NPs with silica Firstly, ethanol and ammonium hydroxide were added into 0.5 mL of TSC@Fe3O4 NPs containing solution The mixture was then passed through sonication treatment in 30 mins Next, 0.45 mL of TEOS was subsequently added to the mixture under vigorous stirring in 12 hrs in order to obtain the silica coated Fe3O4 nanoparticles (denoted as SiO2@Fe3O4 NPs) Afterwards, the separation and washing treatment of SiO2@Fe3O4 NPs were also carried out using the same aforementioned procedure RESULTS AND DISCUSSION 3.1 Effect of surface functionalization In order to investigate functional groups of surface modified Fe3O4 NPs, FT-IR spectra of Fe3O4 NPs, TSC@Fe3O4 NPs and SiO2@Fe3O4 NPs were recorded As shown in Figure 1, three characteristic peaks of Fe3O4 NPs were observed at 583 cm-1, 1616 cm-1 and 3360 cm-1, which correspond to the stretching vibrations of Fe-O, bending and stretching vibrations of O-H, respectively After the treatment with TSC, other two new peaks were also recorded at 1402 cm-1 and 1610 cm-1 (Figure 1b) which are characteristic peaks of –COO– bonds due to successful surface functionalization of Fe3O4 NPs with TSC through the carboxylic groups Interestingly, those aforementioned peaks were almost vanished or weaken in intensity after the surface coating of Fe3O4 NPs with silica (Figure 1c), indicating strong interaction between silanol groups of silica and surface hydroxyl and carboxylic groups of modified Fe3O4 NPs The presence of silica outer-coated Fe3O4 NPs layer can be evidenced by formation of an intensive peak at 1091 cm-1 and other less intensive peaks at 803 cm-1 and 627 cm-1, which are indicative of Si-O-Si and Si-C bonds, respectively Additionally, a small peak of Si-OH bond was also observed at 963 cm-1, probably due to incomplete condensation of TEOS substance 162 Synthesis and characterization of silica coated magnetic iron oxide nanoparticles Figure FT-IR spectra of a) Fe3O4 NPs, b) TSC@Fe3O4 NPs, c) SiO2@Fe3O4 NPs 3.2 Study of crystallinity The crystalline structure of the as-synthesized NPs was investigated through XRD patterns, as indicated in Figure For Fe3O4 NPs, all diffraction peaks of the XRD patterns can be easily indexed to a pure cubic phase of Fe3O4 (JCPDS No 65-3107) (Figure 2a) The characteristic peaks were recorded at 2θ = 30.2°, 35.4°, 43.1°, 53.2°, 56.9°, and 62.5° which represent corresponding indices (220), (311), (400), (422), (511), and (440) [8] The average particle size of Fe3O4 NPs calculated using the Debye–Scherrer formula from the refection peak of (311) is about 13.9 nm [9] It should be noted that the TSC functionalization did not lead to the phase change In contrast, the silica coating resulted in a decrease in the intensity of characteristic peaks of Fe3O4, and the presence of the amorphous silica matrix observed at 2θ = 14.6 [10], probably due to thick SiO2 coating Figure XRD spectra of Fe3O4 NPs, TSC@Fe3O4 NPs and SiO2@Fe3O4 NPs 3.3 Structural morphology TEM images shown in Figure revealed structural morphology of Fe3O4 NPs and SiO2@Fe3O4 NPs It is obvious that Fe3O4 NPs possess polydispersion with the average particle size of 13.7 nm (Figure 3a,e) which is consistent with the XRD results After modification with TSC, there is not much change in particle size which was determined as 16.8 nm (Figure 3e) 163 Minh-Tri Nguyen-Le et al The particles became larger after the coating with silica At this time, SiO2@Fe3O4 NPs revealed a mosaic structure in which SiO2 acts as an outer layer of multi-core Fe3O4 NPs (Figure 3c) 3.4 Thermal stability Thermal stability of Fe3O4 NPs, TSC@Fe3O4 NPs and SiO2@Fe3O4 NPs was explored by TGA (Figure 4) Accordingly, all samples exhibited a weight loss of % – % below 200 oC due to desorption of adsorbed water [11, 12] At temperatures above 200 oC, Fe3O4 NPs are not stable, probably due to oxidation of Fe3O4 into more thermal stable compound Fe2O3 This statement is also true for TSC@Fe3O4 A significant weight loss of 6.7 % above 200 oC was found for TSC@Fe3O4, which can be ascribed to the decomposition of surface functional groups of modified Fe3O4, as well as transformation of Fe3O4 into Fe2O3 Interestingly, after surface coating with silica, SiO2@Fe3O4 NPs revealed negligible weight loss above 200 oC, indicating highly thermal stable state The results demonstrated that SiO2 acts as a protective layer to prevent Fe3O4 NPs from the oxidation Figure TEM images and size distribution of Fe3O4 NPs (a, b) and SiO2@Fe3O4 NPs (c,d); DLS particle size distribution (e) of Fe3O4 (the solid line), TSC@Fe3O4 NPs (the dotted line) and SiO2@Fe3O4 NPs (the dashed line) Figure TGA of Fe3O4 NPs, TSC@Fe3O4 NPs and SiO2@Fe3O4 NPs 164 Synthesis and characterization of silica coated magnetic iron oxide nanoparticles 3.5 Magnetic properties The magnetization versus of Fe3O4 NPs, TSC@Fe3O4 and SiO2 coated Fe3O4 NPs samples were measured in the field scanning from -15 to 15 kOe, and the curves are shown in Fig From Figure 5, one can see that Fe3O4 NPs, TSC@Fe3O4 and SiO2 coated Fe3O4 NPs are all superparamagnetic because no hysteresis loop can be observed [13-16] The saturation magnetization of Fe3O4 NPs is 45.8 emu/g, which is higher than that of TSC@Fe3O4 (~14.6 emu/g), SiO2 coated Fe3O4 NPs (~13.4 emu/g) due to the functionalization and the thick silica shell layer (~ 15 nm), respectively Figure Magnetization of superparamagnetic Fe3O4 NPs, TSC@ Fe3O4 NPs and SiO2@Fe3O4 NPs CONCLUSIONS We demonstrated an effective method for preparation of SiO2 coated Fe3O4 superparamagnetic nanoparticles with saturation magnetization of 13.4 emu/g through a mild synthetic conditions The SiO2 coated Fe3O4 superparamagnetic nanoparticles revealed high thermal stability and superparamagnetic property, which can be used in broad applications including MRI, drug delivery and therapeutic fields Acknowledgements This study was funded by the National Foundation for Science and Technology Development (Grant No 104.03-2018.46) REFERENCES Mahdavi M., Ahmad M B., Haron M J., Namvar F., Nadi B., Rahman M Z., Amin J Synthesis, surface modification and characterisation of biocompatible magnetic iron oxide nanoparticles for biomedical applications, Molecules 18 (7) (2013) 7533-7548 Gupta A.K and Wells S - Surface-modified superparamagnetic nanoparticles for drug delivery: preparation, characterization, and cytotoxicity studies, IEEE Trans Nanobiosci (1) (2004) 66-73 Arbab A.S., Bashaw L A., Miller B R., Jordan E K., Lewis B K., Kalish H., Frank J A - Characterization of biophysical and metabolic properties of cells labeled with superparamagnetic iron oxide nanoparticles and transfection agent for cellular MR imaging, Radiology 229 (3) (2003) 838-846 165 Minh-Tri Nguyen-Le et al Reimer P and Weissleder R - Development and experimental use of receptor-specific MR contrast media, Der Radiologe 36 (2) (1996) 153-163 Pankhurst Q A., Connolly J., Jones S K and Dobson J - Applications of magnetic nanoparticles in biomedicine, J Phys D: Appl Phys 36 (13) (2003) R167 Minko S - Grafting on solid surfaces: “Grafting to” and “grafting from” methods, Polym Surf Interfaces (2008) 215-234 Li Y S., Church JS., Woodhead A L., Moussa F - Preparation and characterization of silica coated iron oxide magnetic nano-particles, Spectrochim Acta, Part A 76 (5) (2010) 484-489 Liang X., Shi H., Jia X., Yang Y., Liu X.- Dispersibility, shape and magnetic properties of nano-Fe3O4 particles, Mater Sci Appl (2011) 1644-1653 Feng B., Hong R Y., Wu Y J., Liu G H., Zhong L H., Zheng Y , Ding J M., Wei D G - Synthesis of monodisperse magnetite nanoparticles via chitosan–poly (acrylic acid) template and their application in MRI, J Alloys Compd 473 (1) (2009) 356-362 10 Jain T K., Morales M A., Sahoo S K., Leslie-Pelecky D L., Labhasetwar V - Iron oxide nanoparticles for sustained delivery of anticancer agents, Mol Pharmaceutics (3) (2005) 194-205 11 Nguyen-Le M T., Lee B K - High temperature synthesis of interfacial functionalized carboxylate mesoporous TiO2 for effective adsorption of cationic dyes, Chem Eng J 281 (2015) 20-33 12 Nguyen-Le M T., Lee B K - Novel fabrication of a nitrogen-doped mesoporous TiO2nanorod titanate heterojunction to enhance the photocatalytic degradation of dyes under visible light, RSC Advances (37) (2016) 31347-31350 13 Glaria A., Soulé S., Hallali N., Ojo W.S., Mirjolet M., Fuks G., Cornejo A., Allouche J., Dupin J C., Martinez H., Carrey J., Chaudret B., Delpech F., Lachaize S., Nayral C.Silica coated iron nanoparticles: synthesis, interface control, magnetic and hyperthermia properties, RSC Advances (56) (2018) 32146-32156 14 Minh T D., Lee B K., Nguyen-Le M T - A Novel Framework of Ternary Fe3O4@γAPTES@rGO Nanohybrid by [CH3OH]-Soluble Distribution for Synergistic Removal of 1,2,3-Benzotriazole, Macromol Res 26 (8) (2018) 763-773 15 Hoang T T T., Nguyen Tran D H., Bach L G., Vu-Quang H., Nguyen D C., Park K D., Nguyen D H - Functional Magnetic Core-Shell System-Based Iron Oxide Nanoparticle Coated with Biocompatible Copolymer for Anticancer Drug Delivery, Pharmaceutics 11(3) (2019) 120 16 Le Thi T N., Nguyen T H., Hoang D Q., Tran T V., Nguyen N T., Nguyen D H Development of new magnetic nanoparticles: Oligochitosan obtained by γ-rays and – coated Fe3O4 nanoparticles, Appl Surf Sci 422 (2017) 863-868 166 .. .Synthesis and characterization of silica coated magnetic iron oxide nanoparticles Recently, advances in nanotechnology have led to a number of diverse applications of nanomaterials Magnetic iron. .. TGA of Fe3O4 NPs, TSC@Fe3O4 NPs and SiO2@Fe3O4 NPs 164 Synthesis and characterization of silica coated magnetic iron oxide nanoparticles 3.5 Magnetic properties The magnetization versus of Fe3O4... small peak of Si-OH bond was also observed at 963 cm-1, probably due to incomplete condensation of TEOS substance 162 Synthesis and characterization of silica coated magnetic iron oxide nanoparticles

Ngày đăng: 13/01/2020, 06:58

Từ khóa liên quan

Tài liệu cùng người dùng

  • Đang cập nhật ...

Tài liệu liên quan